Stratiform press pads and methods for use thereof in laminating flexible printed circuits

ABSTRACT

An article of manufacture and method for assisting the lamination of printed circuits in a flat bed press, in which a stratiform sheet has a thermoplastic layer, a polymeric release layer on one side, a polymeric stabilizing layer having a melting point higher than the laminating temperature peak on the other side, both bonded to the middle thermoplastic layer which has a glass transition point lower than the laminating temperature peak, and a melting point higher than the peak, and the sheet is characterized by substantial freedom from creases, trapped gases, and contaminants between the layers, and the improved method using the stratiform sheet in a flat bed press operation.

This application is a continuation of copending application Ser. No. 793,452, filed Oct. 28, 1985, which in turn was a continuation of application Ser. No. 582,303, filed Feb. 22, 1984, now abandoned.

BACKGROUND OF THE INVENTION

This invention relates to improvements in methods and materials for laminating printed circuits at low pressures on flat bed presses.

In the manufacture of flexible and flat cable circuits, layers of high dielectric strength plastic films with low shrinkage and good stability at high temperatures are first combined with copper or other conductive metal by an additive or subtractive process and electrical circuits are produced by etching or deposition of these metals on the plastic surface. These circuits are then covered by a layer of similar adhesive coated plastic dielectric film to protect and insulate the finished circuit. Holes may be punched or drilled in the layers to allow for connections to the finished circuit.

The circuit assembly is then laid up with a protective cap in single or multiple layers (up to 20 plus) and then laminated under heat (ambient--400 degrees F.) and pressure (250 to 400 p.s.i.) taking extreme care to register the circuits and drilled holes. This process is normally performed in a flat bed laminating press by the operator of the press, using pad materials consisting of multiple layers piled on between the steel caul plates and the finished circuit. Typically, the first layer, next to the steel plate, is a non-sticking release material such as a tetrafluoroethylene coated fiberglass cloth. The second layer includes multiple plies of kraft paper or equivalent cellulosic wood product; the third layer consists of one or more plies of a thermoplastic film; and the final layer consists of one or more layers of release materials such as tetrafluoroethylene or polyvinyl fluoride.

The resultant lamelliform pad may include 10 or more loosely piled layers of dissimilar materials, each having two sides presenting up to 20 opportunities for possible contamination. Because each layer is customarily handcut and laid up by hand, there is a high margin for error in the sequencing of dissimilar materials, resulting in defective circuits.

The pads are arranged in a prescribed order on either side of the circuit assembly with the release layer facing the assembly. Multiple circuit assemblies with associated pads are placed in the press to form a book, and the entire book is pressed in one operation to laminate the individual circuit assemblies. When the laminating process is complete the pads are stripped away and the laminated circuit assemblies are removed for further handling.

Among the problems found in the prior art process were erratic results and lamination failures due to errors in selecting and laying up the multiple plies of dissimilar materials, hot spots appearing in the laminate creases, pockets of gas and other contamination trapped in the pad, lateral shifting of the pad materials and the circuit laminate, and moisture absorption by the cellulosic pad.

Accordingly, it is an object of this invention to provide a stratiform sheet, for use in laminating printed circuits, characterized by freedom from included gases, contaminants, and creases;

It is also an object of this invention to provide such a stratiform sheet that achieves substantially more reliable method of preparing the book for the laminating step, and more dependable results.

It is further an object of this invention to provide such a stratiform sheet that achieves more even and rapid heat distribution with uniform pressure to a printed circuit.

It is an additional object of this invention to provide a means for minimizing lateral movement of the components of the book in the laminating process and to provide means and methods of reducing the incidence of rejection of the laminated circuit product due to lamination failures.

Yet another object of this invention is to reduce operator error and increase lamination cycle efficiency.

DEFINITIONS

As used in this specification, "laminating temperature peak" means the highest temperature attained in the book while in the laminating cycle under consideration; "manufacturing cycle time" means the time from the beginning the job of laying up the book for the press through the press cycle time; "press cycle time" means the time elapsed from starting the pressing operation on the book until the time the book is removed from the press to make room for a new book; "melting point" means the transition from solid including glass to liquid; "glass transition point" means the transition between crystalline to plastic (but not liquid) forms.

SUMMARY OF THE INVENTION

Briefly there is provided to achieve for foregoing objects a stratiform sheet useful in a flat press method of laminating printed circuits. The sheet has a polymeric thermoplastic layer having a glass transition point lower than the laminating temperature peak, and a melting point higher than the laminating temperature peak, a polymeric release layer bonded to a first side of the thermoplastic layer, and a polymeric stabilizing layer, having a melting point higher than, and structural integrity at, the laminating temperature peak bonded to the second side of the thermoplastic layer, and means for joining the layers to unite them into a single, stratiform sheet. The sheet is further characterized by freedom from creases, trapped gases and contaminants between the layers of the sheet.

The polymeric thermoplastic layer may be selected from polyesters, polyvinylchlorides, polyethylenes, polycarbonates, acrylics, ABS and co-polymers of the foregoing materials, in thicknesses ranging from about 4 to 15 mils, preferably about 7.5 mils, and having a glass transition point preferably from about 170 degrees to 225 degrees F.

The polymeric release layer is selected from polyvinylfluorides, polytetrafluoroethylenes, polysiloxanes and other polymers with similar release properties, with a thickness from about 0.1 mil to 4 mils.

The polymeric stabilizing layer is selected from polyimides, polyesters, polyethersulfones, and preferably, biaxially oriented polyethyleneterephthalates, in thicknesses from about 0.5 to 5 mils, preferably, up to about 0.25 to 5 mils. The means for joining the layers of the sheet may be extrusion laminating from thermoplastic polymers such as polyethylene or a urethane prepolymeric type adhesive dissolved in suitable solvents, varying in thickness from 0.1 mil to 1.5 mil.

As further assistance, means are provided whereby the release layer side and the stabilizing layer side may be distinguished.

The stratiform sheet is utilized in the method of laminating printed circuits in a flat press by providing a work piece comprising one or more circuit assemblies in need of lamination, providing the stratiform sheets herein specified, and arranging each circuit assembly in a book with one of said stratiform sheets on each side of a circuit assembly with the release layers thereof facing the circuit assemblies in the press, then pressing the book for the press cycle time appropriate to the product and thickness of the book. The method is particularly useful in press cycles using temperatures up to about 400 degrees F. and at pressures about 250 to 400 p.s.i. in making flexible printed circuits.

BRIEF DESCRIPTION OF THE DRAWINGS

Turning now to the drawings in which a typical prior art book and a presently preferred embodiment of the improvements of this invention are represented:

FIG. 1 is a schematic representation of the layering of a book for a flat press, including a single flexible printed circuit assembly and a lamelliform pad, by means of the prior art method;

FIG. 2 is a schematic representation of the arrangement of a book including a single flexible circuit assembly and the stratiform sheet means according to this invention;

FIG. 3 shows a stratiform sheet made according to the teachings of this invention; and

FIG. 4 shows the temperature curve in a typical prior art press cycle and the contrasting temperature curve in a press cycle utilizing this invention.

DESCRIPTION OF THE PREFERRED EMBODIMENT

FIG. 1 represents the standard flexible printed circuit industry approach to preparing a book including a flexible printed circuit (a product particularly suited to use of the invention herein) to be laminated in a flat bed press. Between the press platens typically there are disposed, in the following order from top to bottom, a steel-press plate 1, teflon glass cloth 2, multiple layers of kraft paper 3, 4, 5, a four-mil layer of polyethylene 6, a second four-mil layer of polyethylene 7 and a two-mil release film 8 to make a cushion assembly. Then the flexible circuit assembly 9 is inserted and a mirror image (i.e., reverse order) of the arrangement is repeated on the other side of the circuit assembly. The component parts of the flexible printed circuit product, per se, are not shown, it being understood that any suitable flexible, printed circuit assembly to be laminated may become the work piece under consideration.

Multiple stacks of the arrangement between the commonly used glass cloth elements are made to create a book, normally separated by steel plates, and the multiple assemblies are laminated in one pressing.

Many opportunities for error are encountered by press operators in putting together the many layers involved. Errors in selection and sequence of materials are found to be committed by experienced operators. Contamination of the layers is a common hazard. Assemblying the layers by hand may cause creases and create gas pockets. The uneven texture of the cellulosic materials causes hot spots, and the rate of heat distribution and transfer is undesirably low.

Attention is now invited to FIG. 2 wherein a presently preferred embodiment of the improved method and product of this invention are shown: As seen in FIG. 2, the platen 1 and the teflon glass cloth 2 are positioned as in the prior art method, but the elements 3 through 8 of the prior art are replaced in their entirety by a single, unitized laminate pad which is herein referred to as a stratiform sheet 10. The flexible printed circuit assembly 9 (the work piece) is the same. A sheet 10, reversed, is positioned on the second side of the flexible circuit assembly followed by the teflon glass cloth 2 and the steel plate 1 to complete the book. The release layer side 11 of each sheet 10 faces the assembly 9. As in the prior art process, multiple flexible circuit assemblies and pads with additional steel plates are stacked between the two layers of glass cloth 2 to make a complete book to charge the press plate in readiness for laminating.

Turning now to FIG. 3, in which an enlarged representation of the pad 10 is shown, layer 12 is a polymeric release layer such as polyvinylfluoride which can be obtained from DuPont Chemical Company under the trademark TEDLAR 50AM20LH, which is the presently preferred polymeric release layer. Other suitable materials are polytetrafluoroethylene, which can be obtained from the DuPont Chemical Company under the name TEFLON, polysiloxane (silicone) and other polymers with similar release properties. The thickness of layer 12 may vary from 0.1 mil to 4 mils. At more than 4 mils difficulty in conforming to three dimensional products may be experienced.

Layer 14 is a high performance, high temperature adhesive. A presently preferred adhesive may be obtained from Morton Chemical Company under the name LAMAL HSA. It is a two-part urethane, prepolymeric adhesive having a solids content of about 70%, dissolved in isopropanol.

Layer 16 is a polymeric thermoplastic layer which is plastic but not melted, and has good conformability at operating temperatures. The presently preferred thermoplastic is a modified polyester in a thickness of 7.5 mils which is a co-polyester formed from teraphthalic acid and isophthalic acid with cyclohexanedimethanol and which has a glass transition point about 189 degrees F. It may be obtained from Lustro Plastics Co., Saugus, California, under the designation "A150".

Another layer of adhesive 14 is applied to bond the thermoplastic layer 16 and the polymeric stabilizing layer 18.

Layer 18 is a high temperature polymeric layer that remains stable and retains its chemical and dimensional stability at temperatures above the laminating temperature peak. The melting point is 429 degrees F. The presently preferred material is biaxially oriented, polyethyleneteraphthalate made by American Hoechst Corporation under the mark Hostaphan 5000 in thicknesses about 0.25 mil to 1.4 mil. The function of this layer is to prevent significant lateral movement of the thermoplastic layer 16 when it is in a plastic state.

The function of the thermoplastic layer 16 is to transmit pressure uniformly from the smooth platen to the three dimensional laminate under the conditions of temperature and pressure used to consolidate the laminate. It is necessary that all parts of the encapsulated printed circuit be in intimate contact with the thermosetting plastic (dielectric) which encapsulates it, and that there be no voids or unbonded areas between the circuit and the plastic (dielectric).

A facet of the problem is that if the thermoplastic forming polymer melts and flows freely it may encapsulate and seal the entire book of laminates. According to the practice of this invention, the material selected for layers 16 and 18 will have a melting point above the laminating temperature peak to avoid the liquid state of laminating process temperatures during the press cycle.

If the melt reduces the thermoplastic layer to a thickness that is thinner than the differences between the peaks and valleys in the cross-section of the three dimensional flexible printed circuit the thermoplastic layer loses its ability to conform to the profile of the circuit, and thereby fails in its function of evenly distributing heat and pressure.

Fortuitously, it was discovered that the stabilizing layer solved other problems such as hot spots and poor thermal transmission in the cellulosic material of the prior method.

Normally, the laminating cycle is operated at low pressures for no more than a one hour cycle time, but in some cases the cycle time is substantially longer. In such case a polymer that has longer stability at that operating temperature may be selected for layer 18. A polymer made by DuPont Chemical Company under the trademark Kapton is suitable for the longer cycle time. Other considerations are that the polymers selected should be non-reactive, and that the materials have stability at operating temperatures, to avoid chemical breakdown and significant loss of mechanical properties due to thermal degradation. Other suitable polymers are obtainable from ICI Chemical Company under the trademark Melinex, and from American Hoechst Corporation under the trademark Hostaphan and from DuPont under the trademark Mylar.

Among the other benefits obtained from use of the stratiform sheet of this invention there have been found an absence of creases, entrapped gases and other contaminants, shrinkage is minimized, and a more uniform distribution of heat and pressure is maintained throughout the laminating cycle wherein the thermoplastic layer goes through its glass transition stage and back, attributable, it is thought, to the quick initial conformance with pressure and continued conformance with flow in the thermoplastic layer. The results obtained from the product and method of this invention are more reliable, due to the combination of materials and reduction of operator error.

The use of kraft paper is avoided altogether and, fortuitously, materials have been provided in the preferred embodiment that will cover a broad range of pressing conditions and most of the pressing requirements encountered in the flexible printed circuit art.

As will be explained in greater detail hereafter the stratiform sheets are made by continuous roller process laminating with heat and pressure, whereby the layers of the stratiform sheet are cemented together by adhesives and are rolled and smoothed to make intimate contact, one layer to another, resulting in an absence of air pockets and creases. The process is carried out in a clean room which produces a contamination free product.

MANUFACTURE OF STRATIFORM SHEET MATERIAL

The stratiform sheet material of this invention is manufactured on a continous web laminating system where a suitable adhesive is applied to a roll of the thermoplastic material. It is then passed through an oven to remove the solvent and a release layer is applied to the adhesive layer using a heated nip and the resulting laminate is reversed and suitable adhesive is applied to the other side of the thermoplastic layer. It goes through the oven to remove the solvent, and the stabilizing layer is applied to the second adhesive treated side using a heated laminating nip and the continuous sheeting is collected on another roll. From there it may be cut to specifically desired sizes suitable for immediate insertion into a book for use in a press, or it may be shipped in roll form to a remote location for processing in that manner. An example of the manufacture of the invention follows.

EXAMPLE I

To a roll of a co-polyester formed from terephthalic acid and isophthalic acid with cyclohexanedimethanol and whose glass transition point is 189 degrees F. and whose sheet thickness is 7.5 mils (obtained from Lustro Plastics Co., Saugus, California under its designation A150) there was applied a two-part urethane prepolymeric adhesive (obtained from Morton Chemical Company under the name Lamal HSA) by means of a standard gravure coating head. The coated co-polymer was sent through an oven to remove the solvents from the adhesive and a roll of polyvinylfluoride (obtained from DuPont Chemical Company under the brand name TEDLAR 50AM20LH) was laminated to the adhesive-treated side with a hot laminating nip and collected on a second roll.

The second roll was passed through the gravure apparatus again to apply the Lamal adhesive to the opposite side of the A150 co-polymer. The coated sheet was again passed through the oven to remove the solvents and laminated to a roll of polyethyleneteraphthalate (obtained from American Hoechst Company, trademarked Hostaphan 5000), through a hot laminating nip. The resulting stratiform sheet was collected n a roll for storage. At a subsequent time it was formed into pads of a suitable size for inclusion in a book of flexible printed circuit laminates for processing in a flat bed press.

Optionally, the means of manufacture might be a one pass coating operation, and be done with a variety of coating methods such as, for example, Meyer rod, air knife or reverse roll coating offset gravure.

METHOD OF USE OF THE STRATIFORM SHEET

The stratiform sheet of this invention replaces multiple layers of dissimilar materials used in the flat bed press method of forming flexible printed circuits under low pressure and heat. Whereas, formerly, the press operator was obliged to cut and lay up as many as 20 different layers of paper and plastic materials in the method of this invention, a single stratiform sheet placed on each side of the circuit assembly will suffice.

In the method of this invention, which is particularly useful in laminating flexible printed circuits in a flat bed press, one or more circuit assemblies are provided as a work piece, a single stratiform sheet is arranged on each side of a circuit assembly with the release layer of each sheet facing a circuit assembly in the press. The book of as many circuit assemblies as desired is arranged in the press between teflon glass cloth layers and steel press plates at each end and between each repetition of circuit assembly and associated stratiform sheets. The book is then pressed at temperatures ranging from room temperature up to about 400 degrees F., typically about 350-380 degrees F. and at pressures between 250-400 p.s.i.

Some of the advantages enjoyed by use of the method utilizing the stratiform sheet is that the time consuming chores of cutting and sequencing the layers at the press are entirely eliminated, resulting in a shorter manufacturing cycle time. The human error encountered in cutting and putting the layers together is avoided and consequently the chances of ruining an expensive work piece is almost entirely eliminated.

Identifying indicia are provided as matte surface on one side of the sheet and smooth on the other side.

Examples of the use of product and method of this invention follow.

EXAMPLE II

A book for press lamination is made up of caul plate, glass cloth, a stratiform sheet of this invention, flexible circuit assembly in need of lamination, stratiform sheet, glass cloth and caul plate, in that order, with the release layers of the stratiform sheets facing the circuit assembly.

A typical circuit assembly was used as the work piece. The stratiform sheet is provided with matte finish on the release layer side and smooth finish on the stabilizing layer side.

The book is assembled at the press site and loaded to a flat bed laminating press. The press cycle is carried out for 80 minutes at 300 p.s.i. The laminating temperature peak is 360 degrees F. Table 1 is a tabulation of temperature progression against time.

The work piece is removed from the press. Upon examination it is found to be well formed and free of defects.

EXAMPLE III

To compare the results of the method and product of the invention with the prior art, another run was made using the same circuit assembly as in Example II and a cushion assembled according to present industry practices as illustrated in FIG. 1 of the drawings.

The time versus temperature results from Example III are shown in Table 2.

The combined data are plotted on the time versus temperature curves in FIG. 4 of the drawings.

                  TABLE 1                                                          ______________________________________                                         Time: 0           25 min.   65 min.  80 min.                                   Temp: 70 degrees F.                                                                              360 degrees                                                                              360 degrees                                                                             70 degrees                                ______________________________________                                    

                  TABLE 2                                                          ______________________________________                                         Time: 0           45 min.   85 min.  120 min.                                  Temp: 70 degrees F.                                                                              360 degrees                                                                              360 degrees                                                                             70 degrees                                ______________________________________                                    

Because there is no longer a need for purchasing dissimilar materials and storing them at the plant, the logistics of purchasing, transporting, collecting and storing multiple inventories are simplified, with a consequent savings of time and money and space. Greater consistency in the pressing process is obtained by using certain materials. In the stratiform sheets of this invention the materials have been selected to cover a broad range of circuit design requirements thereby reducing the need for ad hoc selections of materials for laminating flexible printed circuits. Furthermore, the floor space now required in the prior art for cutting, assembling and storing the pads at or near the press site (after the materials are removed from the warehouse) has also been avoided. 

What is claimed is:
 1. A separate laminated stratiform press sheet for subsequent use in the flat press process of laminating the components of printed circuits to each other comprising a polymeric thermoplastic layer having a glass transition point lower than the laminating temperature peak and a melting point higher than the laminating temperature peak for uniform transmission of pressure in said subsequent laminating process, said polymeric thermoplastic layer having a first side and a second side, a polymeric release layer having a first side and a second side, a polymeric release layer having a first side bonded to said first side of said thermoplastic layer and having a second side for releasable disposition against a printed circuit to be laminated, a polymeric stabilizing layer having a melting point higher than the laminating temperature peak and having a first side bonded to said second side of said thermoplastic layer for prevention of lateral movement of said thermoplastic layer when in a plastic state in said subsequent laminating process, means for joining said first side of said polymeric release layer to said first side of said thermoplastic layer and said first side of said polymeric stabilizing layer to said second side of said thermoplastic layer to unite said layers in a single, stratiform press sheet, said press sheet being further characterized by substantial freedom from creases, entrapped gases, contaminants between said layers.
 2. The stratiform press sheet of claim 1 wherein said polymeric thermoplastic layer is selected from polyvinylchlorides, polyethylenes, polycarbonates, acrylics, ABS, polyester and co-polymers thereof; said polymeric release layer is selected from polyvinyl fluorides, polytetraflouroethylenes, and polysiloxanes, in a thickness from 0.1 mil to 4 mils, and said polymeric stabilizing layer is selected from polyesters, polyethersulfones, biaxially oriented polyethyleneterephthalates and polyimides.
 3. The stratiform press sheet of claim 1 wherein the polymeric release layer and the polymeric stabilizing layer are joined to the polymeric thermoplastic layer by means of polymeric adhesives.
 4. The stratiform press sheet of claim 3 wherein said adhesive is a two-part urethane prepolymeric adhesive.
 5. The stratiform press sheet of claim 1 wherein said adhesive is a thermoplastic resin selected from extrudable polyethylene and polypropylene.
 6. The stratiform press sheet of claim 1 wherein the means for joining said layers is by extrusion lamination with thermoplastic polymers.
 7. The stratiform press sheet of claim 1 with the addition of means for distinguishing the release layer side from the stabilizing layer side to prevent inadvertent reversal in use.
 8. A charge of material for a flat bed press pad useful in printed circuit lamination comprising a printed circuit assembly and a separate laminated stratiform press sheet wherein the layers of said sheet comprise a polymeric release film layer having a first side for bonding to a thermoplastic polymer layer and a second side for releasable disposition against a printed circuit to be laminated, a thermoplastic polymer layer having a glass transition point lower than the laminating temperature peak and a melting point higher than the laminating temperature peak for uniform transmission of pressure in said printed circuit lamination, said thermoplastic polymer layer having a first side juxtaposed to the first side of said polymeric release layer and having a second side, and a polymeric stabilizing layer having a melting point higher than the laminating temperature peak and having a first side juxtaposed to said second side of said thermoplastic polymer layer and when bonded thereto preventing lateral movement of said thermoplastic layer in a plastic state in a subsequent laminating process, all said layers held together in intimate contact by adhesive means, said stratiform sheet being characterized by substantial absence of creases, gases and contaminants between said layers.
 9. The stratiform press sheet of claim 1 wherein the glass transition point of said thermoplastic polymer is from about 170° F. to about 225° F.
 10. The charge of material of claim 8 wherein the glass transition point of said thermoplastic polymer is from about 170° F. to about 225° F.
 11. The stratiform press sheet of claim 1 wherein the glass transition point of said thermoplastic layer is about 189° F.
 12. The charge of material of claim 8 wherein the glass transition point of said thermoplastic layer is about 189° F.
 13. A separate laminated stratiform press sheet useful in assisting the process of heat forming flexible printed circuits on a flat bed press at low pressure, comprising:(a) an outer stabilizing layer of plastic film for preventing lateral movement of a thermoplastic layer when bonded thereto selected from polyesters, polyethersulfones, polyimides, and biaxially oriented polyethyleneterephthalates which have melting points higher than the laminating temperature peak, in thicknesses from about 0.25 to 5 mils and having two sides; (b) a temperature responsive median layer of plastic film for uniform transmission of pressure in said process of heat forming flexible printed circuits selected from polyvinylchloride, polyethylenes, polycarbonates, acrylics, ABS, polyesters, and co-polymers thereof, in thicknesses thereof from about 4 mils and 15 mils, having a glass transition point lower than the lamination temperature peak and having a first side and a second side, said first side being bonded to one of the two sides of said stabilizing layer; (c) an inner release film selected from polyvinylfluorides, polytetrafluoroethylenes and polysiloxanes in thicknesses from about 0.1 mils to 4 mils and having a first side and a second side of which the first side is bonded to the second of the two sides of said temperature responsive median layer; (d) means for bonding said layers to each other in the order given, selected from compatible polymeric adhesives and (e) means for distinguishing the outer and inner layers to prevent inadvertent reversal of layers from the correct sequence in use.
 14. The separate laminated stratiform press sheet of claim 13 wherein said outer layer is a biaxially oriented polyethyleneterephthalate, said inner layer is polyvinylfluoride, said median layer is a co-polyester formed from terephthalic acid and isophthalic acid with cyclohexanedimethanol in a thickness of 7.5 mils and said adhesive is a two-part urethane prepolymeric adhesive.
 15. The separated laminated stratiform press sheet of claim 13 wherein said means for distinguishing the outer and inner layers thereof is a smooth finish on one side of said sheet and a matte finish on the other side of said sheet. 